Product detail
Magnesia-zirconia Brick
Product Parameters
| 项目 Item |
氧化锆空心球砖 Bubble zirconia Brick |
氧化锆砖 zirconia Brick |
镁锆砖 Magnesia-zirconia Brick |
| 最高使用温度℃ Max service temperature |
2200 | 2200 | —— |
| Zr(hf)O2（%） | 98（含稳定剂） | 98（含稳定剂） | ≥13 |
| MgO(%) | —— | —— | ≥76 |
| SiO2 (%) | ≤0.5 | ≤0.5 | ≤8 |
| Fe2O3 (%) | ≤0.2 | ≤0.2 | ≤0.8 |
| 体积密度(g/cm3) Bulk Density |
≤3.1 | ≥4.5 | ≥3.1 |
| 常温耐压强度(Mpa) Cold Crushing Strength |
≥8 | ≥50 | ≥45 |
| 荷重软化开始温度(℃) (0.2Mpa,0.6%) Refractoriness under Load |
>1700 | >1700 | ≥1600 |
| 重烧线变化率 (%) (1700℃*8h) Reheating Linear Change Rate |
±0.2 | ＜0.5 | —— |
| 热膨胀系数(x10-6) （室温Room Temp. to -1300℃） Coefficient of Thermal Expansion |
7.8 | 8 | —— |
| 典型应用 Typical Application |
使用与大于1750℃的特高温窑炉或侵蚀严重的高温窑炉和窑具。 Mainly used in over1750℃ ultra high temperature kiln or erosion of high temperature furnace and kiln furniture. |
||
Mainly used in over1750℃ ultra high temperature kiln or erosion of high temperature furnace and kiln furniture.