Magnesia Chrome Bricks

Magnesia Chrome Bricks

Magnesia Chrome Bricks


Magnesia-chrome brick is a high-level refractory product material ,which containing MgO and Cr2O3 as the main components, periclase and spinel are the main mineral components.

Email: [email protected]

WhatsApp/Phone Number: +8613592411271

Product detail

Magnesia Chrome Bricks

Magnesia-chrome brick is a high-level refractory product material ,which containing MgO and Cr2O3 as the main components, periclase and spinel are the main mineral components. This type of brick has high refractoriness, high temperature strength, strong resistance to alkaline slag, excellent thermal stability, and certain adaptability to acidic slag. The main raw materials for the manufacture of magnesia chrome bricks are sintered magnesia and chromite. The purity of the magnesia raw material should be as high as possible.

Features

(1).high refractoriness

(2).high temperature strength

(3).strong resistance to alkaline slag

(4).excellent thermal stability

Appplication

Common mag-chrome brick: Cement rotary kiln, glass kiln regenerative chamber, glass tank furnace ,steel furnace lining, refining ladle, non-ferrous metallurgical furnace, lime kiln, mix iron furnace, open hearth furnace.

Direct-Bonded mag-chrome brick : Cement rotary kiln, steelmaking electric furnace lining, refining furnace(RH,VOD,EAF), non-ferrous metallurgical furnace, glass kiln regenerative chamber, lime kiln, mix iron furnace, building materials, copper smelting furnace.

Packaging Details

1.On wooden pallets with plastic cover

2.According to customer’s demands

Product Parameters

Commom Magnesite Chrome Brick

Chemical composition and technical performance Product brand
  SRMG-8 SRMG-12 SRMG-15 SRMG-18
MgO(%) >=65 >=60 >=55 >=52
Cr2O3(%) >=8 >=12 >=15 >=18
SiO2(%) <=1.5 <=1.5 <=1.8 <=1.8
Apparent porosity(%) <=18 <=18 <=18 <=18
Cold crushing strength(MPa) >=40 >=40 >=40 >=40
0.2MPa refractoriness under load T0.6(oC) >=1670 >=1670 >=1670 >=1670
Thermal shock resistance
(1300oC air cooling)
(1100oC water cooling)
>=30
>=6
>=30
>=6
>=30
>=6
 

Fused Magnesite Chrome Brick

Chemical composition and technical performance Product brand
  ERMG-12 ERMG-16 ERMG-20
MgO(%) >=60 >=55 >=50
Cr2O3(%) >=12 >=16 >=20
SiO2(%) <=1.5 <=1.8 <=2.0
Apparent porosity(%) <=16 <=16 <=16
Cold crushing strength(MPa) >=40 >=40 >=40
0.2MPa refractoriness under load T0.6(oC) >=1700 >=1700 >=1700
Thermal shock resistance
(1300oC air cooling)
(1100oC water cooling)
>=15
>=4
>=15
>=4
>=15
>=4